| Category 類 別 |
Trade mark 牌 號 |
Chemical composition 主要成份(%) |
Characteristics & application 特性和用途 |
Equivalent to AWS 相當AWS |
Hardfacing 硬 面 堆 焊 |
S 101 |
C3 Cr28 Ni4 Si3.5 Fe Rem. |
HRc48-54. Resistance to wear, gas corrosion and oxidation. Hardfacing of bucket tooth and case pump. HRc48-54，耐磨、耐氣蝕、抗氧化。堆焊鏟斗齒，泵套 |
|
| S 111 |
C1 Cr29 W5 Co Rem. |
HRc38-47. Resistance to wear and corrosion at high-temperature. Hardfacing of high temperature and pressure valve. HRc38-47，高溫下耐磨、耐蝕。堆焊高溫高壓閥門 |
ECoCr-A | |
| S 112 |
C1.5 Cr29 W8 Co Rem. |
HRc45-50. Resistance to wear and corrosion at high-temperature. Hardfacing of valve and hot-rolling pass. HRc45-50，高溫下耐磨、耐蝕。堆焊閥門，熱軋孔型 |
ECoCr-B | |
| S 113 |
C2.5 Cr30 W17 Co Rem. |
HRc≥55. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of screw charging carriage. HRc≥55，高溫下耐磨、耐熱，但抗沖擊性差。堆焊螺旋送料機用 |
||
| S 114 |
C2.5 Cr30 W12 Co Rem. |
HRc≥53. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of three-cone bit. HRc≥53，高溫下耐磨、耐熱，但抗沖擊較差。堆焊牙輪鉆頭 |
ECoCr-C | |
Copper alloys 銅 合 金 |
S 201 |
Sn1 Si0.3Mn0.3 Cu Rem. |
Good mechanical properties and crack resistance. Gas welding and argon arc welding of red copper. 機械性能好，抗裂性好。紫銅氣焊及氬弧焊用 |
ERCu |
| S 211 |
Si3 Mn1 Cu Rem. |
Good mechanical properties. Argon arc welding of copper alloys and MIG brazing of steel. 機械性能好，銅合金氬弧焊及鋼的MIG釬焊用 |
ERCuSi-Al | |
| S 212 |
Sn5 Cu Rem. |
Wear resistance. Argon arc welding of copper alloys and surfacing of steel. 耐磨性好。銅合金氬弧焊及鋼的堆焊用 |
ERCuSn-A | |
| S 213 |
Sn8 Cu Rem. |
Wear resistance. Argon arc welding of copper alloys and surfacing of steel. 耐磨性好。銅合金氬弧焊及鋼的堆焊用 |
ERCuSn-C | |
| S 214 |
Al7.5 Cu Rem. |
Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel. 耐磨、耐蝕。銅合金氬弧焊及鋼的堆焊用 |
ERCuAl-A1 | |
| S 215 |
Al9 Cu Rem. |
Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel. 耐磨、耐蝕。銅合金氬弧焊及鋼的堆焊用 |
ERCuAl-A2 | |
| S 221 |
Cu60 Sn1 Si0.3 Zn Rem. |
Melting point is about 890℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron. 熔點約890℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵 |
||
| S 221F |
Cu60 Sn1 Si 0.3 Zn Rem. |
S221 welding rod coated with flux. 外涂焊劑的S221焊絲 |
||
| S 222 |
Cu58Sn0.9Si0.1 Fe0.8 Zn Rem. |
Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron. 熔點約880℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵 |
RBCuZn-C | |
| S 222F |
Cu58Sn0.9Si0.1 Fe0.8 Zn Rem. |
S222 welding rod coated with flux. 外涂焊劑的S222焊絲 |
RBCuZn-C | |
| S 223 |
Cu59 Sn0.6 Zn Rem. |
Melting point is about 900℃. Braze welding of copper, steel and cast iron. 熔點約900℃。銅、鋼、鑄鐵釬焊用 |
RBCuZn-A | |
| S 224 |
Cu62 Si0.5 Zn Rem. |
Melting point is about 905℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron. 熔點約905℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵 |
||
| Copper alloys 銅 合 金 |
S 225 |
Cu48 Ni10 Zn Rem. |
Melting point is about 935℃ and high strength. Braze welding of steel, nickel and carbide alloys. 熔點約935℃。高強度,釬焊鋼、鎳及硬質(zhì)合金用 |
RBCuZn-D |
| S 225F |
Cu48 Ni10 Zn Rem. |
S225 welding rod coated with flux. 外涂焊劑的S225焊絲 |
RBCuZn-D | |
| S 226 |
Cu60 Sn0.3 Si0.2 Zn Rem. |
Melting point is about 900℃. Gas welding of brass, also braze welding of copper, steel and cast iron. 熔點約900℃。黃銅氣焊用，也可釬焊銅、鋼、鑄鐵 |
||
| S 227 |
Cu58Sn0.9Ni0.5 Si0.1 Fe0.8 Zn Rem. |
Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron. 熔點880℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵 |
RBCuZn-B | |
| S 229 |
Cu55 Ni6 Mn4 Zn余 |
Melting point is about 920℃, high strength. Braze welding of steel, nickel and hard carbide. 熔點約920℃。高強度,釬焊鋼、鎳及硬質(zhì)合金用 |
||
| Aluminum alloys 鋁 合 金 |
S 301 |
Al≥99.5 |
Good ductility and corrosion resistance. Gas welding and argon arc welding of pure aluminum. 塑性好、耐蝕。純鋁氣焊、氬弧焊用 |
ER1100 |
| S 311 |
Si5 Al Rem. |
Corrosion resistance, wide range of usage. Gas welding and argon arc welding of aluminum alloys other than high magnesium alloys. 抗裂性好，通用性大。鋁合金氣焊、氬弧焊用。不宜用高鎂合金 |
ER4043 | |
| S 321 |
Mn1.3 Al Rem. |
Good corrosion resistance, weldability and ductility. Gas welding and argon arc welding of aluminum alloys. 良好的耐蝕性、可焊性及塑性。鋁合金氣焊、氬弧焊用 |
||
| S 331 |
Mg5 Mn0.4 Al Rem. |
Corrosion resistance and high strength. Argon arc welding of aluminum alloys. 耐蝕，強度高。鋁合金氬弧焊用 |