65Mn彈簧鋼，65Mn彈簧鋼帶，65Mn熱處理鋼帶，65Mn淬火彈簧鋼帶，65Mn軟料彈簧鋼帶，65Mn半硬彈簧鋼帶，65Mn彈簧鋼圓棒，65Mn彈簧鋼線材，65Mn彈簧鋼油淬鋼線，65Mn彈簧鋼熱軋圓棒，65Mn彈簧鋼冷拉圓棒，65Mn彈簧鋼熱軋鋼板，65Mn彈簧鋼冷軋鋼板，65Mn彈簧鋼帶材，65Mn彈簧鋼批發，65Mn彈簧鋼價格，65Mn彈簧鋼規格，65Mn彈簧鋼性能，65Mn彈簧鋼廠家，65mn錳鋼片，彈簧鋼片，

65 mn spring steel, 65 mn spring steel band, 65 mn steel belt heat treatment, 65 mn spring steel quenching zone, soft material 65 mn spring steel, 65 mn half hard spring steel, 65 mn spring steel round bar, 65 mn spring steel wire, 65 mn spring steel oil quenching steel wire, 65 mn spring steel hot rolled round bars, 65 mn spring steel cold-drawn round bar, 65 mn spring steel hot rolled steel, 65 mn spring steel cold rolled steel, 65 mn spring steel strip, 65 mn spring steel wholesale, price of 65 mn spring steel, 65 mn spring steel specifications, the perbance of 65 mn spring steel, 65 mn spring steel manufacturers, 65 mn manganese steel, spring steel,

65Mn彈簧鋼，錳提高淬透性，φ12mm的鋼材油中可以淬透，表面脫碳傾向比硅鋼小，經熱處理后的綜合力學性能優于碳鋼，但有過熱敏感性和回火脆性。用作小尺寸各種扁、圓彈簧、座墊彈簧、彈簧發條，也可制作彈簧環、氣門簧、離合器簧片、剎車彈簧及冷拔鋼絲冷卷螺旋彈簧等。

65mn 強度.硬度.彈性和淬透性均比65號鋼高，具有過熱敏感性和回火脆性傾向，水淬有形成裂紋傾向。退火態可切削性尚可，冷變形塑性低，焊接性差。 受中等載荷的板彈簧，直徑達7-20mm的螺旋彈簧及彈簧墊圈.彈簧環。高耐磨性零件，如磨床主軸.彈簧卡頭.精密機床絲桿.切刀.螺旋輥子軸承上的套環.鐵道鋼軌等。

65Mn彈簧鋼力學性能

●力學性能：

抗拉強度σb (MPa)：825~925

屈服強度 σs (MPa)：≥784(80)

伸長率 δ10 (%)：14~22.5

斷面收縮率 ψ (%)：不大于10

硬度：熱軋,≤302HB;熱軋+熱處理,≤321HB

65Mn彈簧鋼熱處理規范

●熱處理規范及金相組織：

熱處理規范：淬火830℃±20℃,油冷; 回火540℃±50℃(特殊需要時,±30℃)。

金相組織：屈氏體。

●臨界點溫度（近似值）Ac1=726℃，Ac3=765℃，Ar3=741℃，Ar1=689℃，Ms=270℃。

●正火規范:溫度810±10℃，空氣冷卻。[1] 

●交貨狀態：熱軋鋼材以熱處理或不熱處理狀態交貨，冷拉鋼材以熱處理狀態交貨。

●供貨規格：

盤圓：Φ5.5～16mm

鍛材：Φ160～450mm

65Mn彈簧鋼密度

65Mn密度 ρ=7.85克/立方厘米，該鋼可以冷軋成鋼板、鋼帶和鋼絲，制作彈簧。65Mn也可以制作成如鉗工的鑿子、劃針等工具。65Mn鋼可制作一般截面尺寸為8～15mm左右的小型彈簧如各種小尺寸扁、圓彈簧，底墊彈簧、彈簧發條。

760℃×30min保溫，再以20℃/h的冷速冷至700℃×6h再爐冷，得到完全的球化組織，尺寸均勻。

65Mn彈簧鋼重量計算公式

圓鋼：0.00617*直徑*直徑*長度

板材：厚度*寬度*長度*密度